Recently, we have shown that minute Cr additions (typically 0.1 wt%) to Al-Zn alloys solidified in a uniform temperature field lead to the formation of fine equiaxed fcc Al grains [1]. Furthermore, these grains exhibit an unexpectedly large number of twin, ...
In the fabrication of heat-treatable aluminum parts such as AA2618 compressor impellers for turbochargers, solutionizing and quenching are key steps to obtain the required mechanical characteristics. Fast quenching is necessary to avoid coarse precipitatio ...
New data are presented on dynamic measurements of elasticity and anelasticity of several poly- and single crystalline Ni1+xTi1-x alloys for frequencies between 0.05 and 100 kHz over a wide temperature range below room temperature. Anelastic effects, previo ...
In this study, we explored the growth kinetics of the Al-Fe intermetallic (IM) layer at the joint interface of the St-12/Al-5083 friction stir lap welds during post-weld annealing treatment at 350, 400 and 450 degrees C for 30 to 180 mm. Optical microscope ...
Upon solidification, most metallic alloys form dendritic structures that grow along directions corresponding to low index crystal axes, e.g., directions in fcc aluminum. However, recent findings[1,2] have shown that an increase in the zinc content in Al-Zn ...
The influence of the carbon content on the microstructure, phase transformation and hardness of an iron-based cermet is studied. The cermet is constituted by a high-alloyed steel as matrix, and TiCN particles (50 vol.%) as reinforcement. The material is pr ...
We report experimental evidence for three sequential, distinct dynamic regimes in the capillary self-alignment of centimeter-sized foil dies released at large uniaxial offsets from equilibrium. We show that the initial transient wetting regime, along with ...
Intermetallic phases formation is one of the phenomena, which when coupled to thermal and mechanical strains leads to the premature wear of aluminium die casting tools made out of steel. This work focuses on two aspects of this wear problem. The first and ...