The main objectives of this work are 2-fold : The development of a novel type of composite material based on carbon nanofibers supported on sintered metal fibers filters (CNF/SMF) and to explore the use of this material as a catalytic support for a model reaction: selective hydrogenation of acetylene. The advantages of this novel support are: Due to carbon nanofibers, it combines a graphitic structure with a high specific surface area without microporosity. Supported carbon nanofibers can be used in a fixed bed reactor without very high pressure drop. Combination of two materials with high thermal conductivity gives a composite which keeps this property. It is suitable for highly exo/endothermic reactions, diminishing temperature gradients in the catalytic bed. The synthesis of carbon nanofibers on SMF filters was carried out by ethane catalytic decomposition at 655°C directly on metallic filters. An oxidation of SMF followed by a reduction in H2 create surface roughness, leading to a larger area for CNF nucleation. The CNF formation mechanism includes several steps: it starts with carbon deposition on metallic surface followed by its diffusion into the metal leading to carbides formation. When the limit of carbon solubility is attained, a layer of carbon is formed on the surface of metallic fibers. High tension within the bulk metal leads to carbide dissociation and by phase separation to graphite formation, which pushes the metallic particles through the carbon layer. Nickel, stainless steel an Inconel (an alloy of mainly nickel, iron and chromium) filters were used. The latter gave the highest uniformity of the carbon nanofibers layer showing an excellent mechanical stability. In order to control carbon deposition on the filters, a formal kinetic analysis of the decomposition reaction was undertaken. Partial orders of 1 for ethane, -2 for hydrogen and an apparent activation energy of 235 kJ/mol were obtained. The observed kinetics suggests strongly that the C – C bond scission is the rate determining step and not carbon diffusion into the metal which is often reported in the literature. The synthesis procedures like time on stream and reaction temperature were optimized: 1 hour of a mixture C2H6:H2:Ar (3:17:80) decomposition over SMFInconel at 655°C lead to ∼6% of carbon, leading to a CNF layer of 1 µm thickness covering the metallic fibers entirely. This material presents a high specific surface area (22.2 m2/g) and a low pressure drop for the gas flowing through. The carbon nanofibers have a diameter between 20 and 50 nm and a crystalline structure with platelets morphology where the graphene layers are stacked one above the other. Their surface is composed almost exclusively of carbon and hydrogen. Amongst the multiple possible applications of this novel composite material, its use as a catalyst support was assessed. Selective hydrogenation of acetylene was carried out over palladium supported on CNF/SMF and compared with commercial support
Harald Brune, Hao Yin, Wei Fang