Failure of mounting bolt of helicopter main gearbox support strut

Predrag Andric
2016
Journal Articles

Abstract

The mounting bolt of helicopter main gearbox support strut was fractured into two pieces during the flight mission. The fracture occurred at the root of the first engaged thread of the bolt-nut assembly. Visual inspection of the fracture zone revealed cracks, formed by interlinking of corrosion pits, at the almost all thread roots of the bolt. Energy dispersive spectroscopy disclosed significant damage of the cadmium plating as well as the presence of large amounts of corrosion products at the bolt threads. Through the fractography and metallography analysis, it was found that the mounting bolt failed due to hydrogen-induced intergranular stress corrosion cracking (HI-IGSCC). The finite element (FE) analysis confirmed that the crack origin was located at the area with the maximum tensile stress in the bolt. (C) 2016 Elsevier Ltd. All rights reserved.

Official source

https://infoscience.epfl.ch/entities/publication/cb448dc3-b073-4761-8632-3fab9098eb63

About this result

This page is automatically generated and may contain information that is not correct, complete, up-to-date, or relevant to your search query. The same applies to every other page on this website. Please make sure to verify the information with EPFL's official sources.

Predrag Andric
2016
Journal Articles

Abstract

Official source

https://infoscience.epfl.ch/entities/publication/cb448dc3-b073-4761-8632-3fab9098eb63

About this result

Related concepts (32)

Corrosion

Corrosion is a natural process that converts a refined metal into a more chemically stable oxide. It is the gradual deterioration of materials (usually a metal) by chemical or electrochemical reaction with their environment. Corrosion engineering is the field dedicated to controlling and preventing corrosion. In the most common use of the word, this means electrochemical oxidation of metal in reaction with an oxidant such as oxygen, hydrogen or hydroxide. Rusting, the formation of iron oxides, is a well-known example of electrochemical corrosion.

Bolted joint

A bolted joint is one of the most common elements in construction and machine design. It consists of a male threaded fastener (e. g., a bolt) that captures and joins other parts, secured with a matching female screw thread. There are two main types of bolted joint designs: tension joints and shear joints. In a tension joint, the bolt and clamped components of the joint are designed to transfer an applied tension load through the joint by way of the clamped components by the design of a proper balance of joint and bolt stiffness.

Corrosion engineering

Corrosion engineering is an engineering specialty that applies scientific, technical, engineering skills, and knowledge of natural laws and physical resources to design and implement materials, structures, devices, systems, and procedures to manage corrosion. From a holistic perspective, corrosion is the phenomenon of metals returning to the state they are found in nature. The driving force that causes metals to corrode is a consequence of their temporary existence in metallic form.

Related publications (26)

Artificial Hydrophilic Organic and Dendrite-Suppressed Inorganic Hybrid Solid Electrolyte Interface Layer for Highly Stable Zinc Anodes

Lei Zhang, Kangning Zhao

Aqueous zinc-ion batteries (AZIBs) have gained significant attentions for their inherent safety and cost-effectiveness. However, challenges, such as dendrite growth and anodic corrosion at the Zn anode, hinder their commercial viability. In this paper, an ...

Amer Chemical Soc2024

An adaptive phase field approach to 3D internal crack growth in rocks

Tao Xu, Michael Heap, Alexandra Roma Larisa Kushnir

Modeling the 3D internal crack under compression entails complex fracture mechanics (mode I-II-III fracture), resulting in substantial computational costs and challenges in characterizing fracture morphology characterization for Phase Field Method (PFM) si ...

2024

Influence of fiber orientation on the tensile behavior of UHPFRC and reinforced UHPFRC under static and fatigue loadings

Jian Zhan

Ultra-high performance fiber reinforced cementitious composite (UHPFRC) is a modern class of cementitious building materials. Because of its superior mechanical properties and durability, it is increasingly used globally to rehabilitate, strengthen and mod ...

EPFL2024