The effect of defect location on coating fragmentation patterns under biaxial tension

Fragmentation of a coating possessing orthogonal preferential crack propagation directions is modeled for equibiaxial tensile loading. Two plausible cracking scenarios are compared, caused by flaws randomly distributed over the area of the coating or along the coating fragment edges. The two fragmentation scenarios considered are shown to yield qualitatively different fragment patterns.