Publication
Inorganic metal halide perovskites such as CsPbI3 are promising for high-performance, reproducible, and robust solar cells. However, inorganic perovskites are sensitive to humidity, which causes the transformation from the black phase to the yellow & delta;, non-perovskite phase. Such phase instability has been a significant challenge to long-term operational stability. Here, a surface dimensionality reduction strategy is reported, using 2-(4-aminophenyl)ethylamine cation to construct a Dion-Jacobson 2D phase that covers the surface of the 3D inorganic perovskite structure. The Dion-Jacobson layer mainly grows at the grain boundaries of the perovskite, effectively passivating surface defects and providing favourable interfacial charge transfer. The resulting inorganic perovskite films exhibit excellent humidity resistance when submerged in an aqueous solution (isopropanol:water = 4:1 v/v) and exposed to a 50% humidity air atmosphere. The Dion-Jacobson 2D/3D inorganic perovskite solar cell (PSC) achieves a power conversion efficiency (PCE) of 19.5% with a Voc of 1.197 eV. It retains 83% of its initial PCE after 1260 h of maximum power point tracking under 1.2 sun illumination. The work demonstrates an effective way for stabilizing efficient inorganic perovskite solar cells. CsPbI3 perovskites suffers fast transfer to non-perovskite phase, especially exposed to humidity. Using 2-(4-aminophenyl)ethylamine cation to construct a Dion-Jacobson 2D phase that covers the 3D inorganic perovskite surface, the obtained 2D/3D perovskite films exhibit excellent humidity resistance and higher temperature stability, resulting in improved efficiency and operational stability in solar cells.image